Dr. Alan Turnbull OBE FRS FREng获得李薰讲座奖
 
2017-11-10 | 文章来源:外事办        【 】【打印】【关闭

  Topic: Characterising the early stages of crack development in environmentally assisted cracking 

  Speaker: Dr. Alan Turnbull OBE FRS FREng 
        National Physical Laboratory, UK 

  Abstract: 

  A very brief introduction to NPL and the research of the Electrochemistry Group will be presented initially. The main thrust of the presentation will be an overview of corrosion research to characterise the early stages of crack development in environment assisted cracking, focusing particularly on pitting, the pit-to-crack transition, and the measurement of crack growth rate in the small and long crack growth regime. The impact on corrosion and cracking of surface grinding induced changes in near–surface material and mechanical properties is highlighted, noting that awareness of this aspect in the corrosion community still remains limited. A major feature of the presentation is the remarkable insight into the evolution of small cracks from corrosion pits provided by advanced 3D imaging (XRT and FIB-SEM) and supportive finite element analysis. Finally, measurement of corrosion fatigue and stress corrosion small crack growth rate in 12 Cr steam turbine blade steel is presented and discussed in the context of the electrochemical crack size effect. 

文档附件

相关信息
·李薰奖获得者Alan Turnbull博士访问金属所
联系我们 | 友情链接
地址: 沈阳市沈河区文化路72号 邮编: 110016
运维邮箱: office@imr.ac.cn
中国科学院金属研究所 版权所有 辽ICP备05005387号-1

官方微博

官方微信